Reactive diluents

Product	Chemical name	Structure	CAS	EEW g/eq	Viscosity at 25°C mPa•s	Gardner colour max	Water solubility	Further attributes	Industries	Attributes
ipox RD 14	Neopentylglykol-diglycidylether		17557-23-2	150 – 160	15 – 25	2		comparable to ipox RD 18; improved price/performance ratio; low volatility
ipox RD 14 eco	Neopentylglykol-diglycidylether		17557-23-2	150 – 160	15 – 25	2		comparable to ipox RD 18; improved price/performance ratio; low volatility
ipox RD 17	2-Ethyl-Hexyl-glycidylether		2461-15-6	210 – 230	2 – 4	1		very good dilution performance; low odor; self-emulsifying character
ipox RD 18	1,6-Hexandiol-diglycidylether		933999-84-916096-31-4	147 – 161	15 – 25	1		mechanical properties are little affected; very good chemical resistance
ipox RD 19	Polyoxypropylenglycol-diglycidylether		26142-30-3 Polymer	280 – 350	30 – 70	1		results in impact resistant resin systems; hydrophobic character
ipox RD 20	Trimethylolpropane-polyglycidylether		30499-70-8 Polymer	140 – 150	120 – 180	2		accelerating effect; high degree of crosslinking; glass transition temperature is only slightly affected
ipox RD 21	Poly(tetramethylene-oxide)-diglycidylether		26951-52-0 Polymer	395 – 445	140 – 190	2		results in impact resistant resin systems; hydrophobic character
ipox RD 24	C12-C14-glycidylether		68609-97-2	270 – 313	5 – 10	1		very good dilution performance; hydrophobic character; only low volatility
ipox RD 3	1,4-Butanediol-diglycidylether		2425-79-8	130 – 145	12 – 22	1		best difunctional thinner; mechanical properties are little affected; very good solvent resistance
ipox RD 61-1	C12-C14-EOx-glycidylether	-	Polymer	470 – 500	15 – 25	2		results in impact resistant resin systems; hydrophobic character

Bonding agents / crosslinkers

Product	Chemical name	Structure	CAS	EEW g/eq	Viscosity at 25°C mPa•s	Gardner colour max	Water solubility	Further attributes	Industries	Attributes
ipox CL 12	Glycerol-polyglycidylether		90529-77-4	140 – 150	160 – 200	1		good dilution performance; very good wetting performance; hydrophilic character
ipox CL 12 eco	Glycerol-polyglycidylether		90529-77-4	140 – 150	160 – 200	1		good dilution performance; very good wetting performance; hydrophilic character
ipox CL 16	Pentaerythritol-polyglycidylether		3126-63-430973-88-7 Polymer	156 – 170	900 – 1200	2		aliphatic epoxy resin; high degree of crosslinking
ipox CL 16 eco	Pentaerythritol-polyglycidylether		3126-63-430973-88-7 Polymer	156 – 170	900 – 1200	2		aliphatic epoxy resin; high degree of crosslinking
ipox CL 60	Polyglycidylether of ethoxylated Trimethylolpropane	-	Polymer	370 – 490	240 – 380	4		aliphatic epoxy resin; very hydrophilic character; very soluble in water
ipox RD 20	Trimethylolpropane-polyglycidylether		30499-70-8 Polymer	140 – 150	120 – 180	2		good dilution performance; aliphatic epoxy resin; hydrophobic character
ipox RD 20 eco	Trimethylolpropane-polyglycidylether		30499-70-8 Polymer	140 – 150	120 – 180	2		good dilution performance; aliphatic epoxy resin; hydrophobic character

Cycloaliphatic epoxy resins

Product	Chemical name	CAS	EEW g/eq	Viscosity at 25°C mPa•s	Gardner colour max	Further attributes	Industries	Attributes
ipox ER 15	Hydrogenated BPA-diglycidylether	13410-58-7 30583-72-3	225 – 245	2000 – 3700	1	cycloaliphatic epoxy resin; very hydrophobic character
ipox ER 15 eco	Hydrogenated BPA-diglycidylether	13410-58-7 30583-72-3	225 – 245	2000 – 3700	1	cycloaliphatic epoxy resin; very hydrophobic character
ipox ER 15-1	Hydrogenated BPA-diglycidylether	13410-58-7 30583-72-3	210 – 225	1500 – 2500	1	cycloaliphatic epoxy resin; very hydrophobic character

Modified amine hardeners

Product	Chemical base	HEW g/eq	Viscosity at 25°C mPa•s	Gardner colour max	Gel time (min)100g,23°C,DGEBA	Description	Without VOCs*	Primers	Mortarsscreeds	Pigmentedcoatings	Decorative coatings	Industries	Attributes	Ingredients	Alkylphenol free
ipox EH 2041	modified cycloaliphatic amines	95	125 – 225	2	50	excellent surfaces,very good chemical resistance,curing at T > 10°C,long working time,low yellowing tendency							-	-
ipox EH 2042	modified cycloaliphatic amines	95	275 – 375	2	25	faster through-curing than EH 2041,very good curing at T > 7°C							-	-
ipox EH 2047	modified cycloaliphatic amines	75	200 – 300	1	30	excellent surfaces, curing at T > 10°C, low yellowing tendency								-
ipox EH 2049	modified cycloaliphatic amines	95	100 – 200	1	60	excellent surfaces, long working time, very low yellowing tendency, very good early water resistance		-	-	-	-		-	-
ipox EH 2061	modified cycloaliphatic amines	92	150 – 250	1	100	excellent surfaces, long working time, very low tendency to yellowing								-
ipox EH 2062	modified cycloaliphatic amines	100	350 – 600	1	45	faster through-curing than EH 2061, very good chemical resistance, very low yellowing tendency								-
ipox EH 2072	modified cycloaliphatic amines	115	350 – 450	1	70	excellent surfaces, long working time, very low yellowing tendency, very good early water resistance								-
ipox EH 2078	modified cycloaliphatic amines	122	3500 – 6500	3	30	excellent surfaces, very good chemical resistance, curing at T > 10°C			-		-			-
ipox EH 2081-1	modified cycloaliphatic amines	63	60 - 160	11	70	Hardener for water washable jointing compounds		-	-	-	-			-
ipox EH 2082	modified cycloaliphatic amines	44	75 - 175	3	70	emulsifiable, together with ipox ER 1030-6W for water-washable grouts		-	-	-	-			All ingredients listed in the "Coating Guideline", Annex 1, Federal Environment Agency (as of 03/2016)
ipox EH 2212	MXDA-Mannichbase	85	450 – 750	5	15	cures at T > 5°C, very good chemical resistance, reactive accelerator					-			-
ipox EH 2213	MXDA-Mannichbase	75	400 – 600	5	15	lower viscosity than EH 2212, improved surface properties					-			-
ipox EH 2216	modified cycloaliphatic amines	64	650 – 850	5	12	low-temperature curing agent for epoxy resins, very fast through-curing		-	-	-	-			-
ipox EH 2240	MXDA-ACN-Adduct	102	120 – 220	2	> 4h	for impact resistant EP systems with high chemical resistance, co-hardener					-			-
ipox EH 2350	modified polyaminoamide	115	600 – 1200	8	60	excellent adhesion to damp substrates and steel, low viscosity, very hydrophobic, can be accelerated with EH 2212 or EH 2216				-	-		-	-
ipox EH 2900	Tertiary amine	-	90 – 300	4	-	Catalyst, Accelerator					-			-

Water-emulsifiable epoxy resins

Product	Chemical base	EEW g/eq	Viscosity at 25°C mPa•s	Gardner colour max	Further attributes	Application	Ingredients	Industries	Attributes
ipox ER 1030-6W	Bisphenol-A-diglycidylether difunctional RD	165 – 185	500 – 800	2	100	water emulsifiable epoxy resin with ipox EH 2082 water washable grouts	All ingredients listed in the "Coating Guideline", Annex 1, Federal Environment Agency (as of 03/2016)
ipox ER 1030W	Bisphenol-A-diglycidylether polymeric reactive emulsifier	188 – 198	9000 - 13000	3	100	water emulsifiable epoxy resin for the preparation of epoxy resin emulsions, 100% reactive emulsifier	All ingredients listed in the "Coating Guideline", Annex 1, Federal Environment Agency (as of 03/2016)
ipox ER 1031W	Bisphenol-A-diglycidylether emulsifier	180 – 200	7500 - 12000	1	100	water emulsifiable epoxy resin for the production of epoxy resin emulsions	All ingredients listed in the "Coating Guideline", Annex 1, Federal Environment Agency (as of 03/2016)
ipox ER 1035W	water based epoxy resin	255 – 285	50 – 250	weiße Emulsion	66 – 68	liquid resin emulsion for the production of waterborne paints and coatings	-
ipox ER 1100-8W	Bisphenol-A/F-diglycidylether difunctional RD	165 – 185	750 – 950	1	100	water emulsifiable epoxy resin	-
ipox ER 1100W	Bisphenol-A/F-diglycidylether	180 – 190	6000 – 8000	2	100	water-based emulsion paints and adhesives	-

Modified epoxy resins

Product	Chemical base	EEW g/eq	Viscosity at 25°C mPa•s	Gardner colour max	Application	Industries	Attributes
ipox ER 1020	Bisphenol-A-diglycidylether monofunctional RD	190 – 205	900 – 1500	1	solvent-free epoxy systems, hydrophobic character, optimized wetting of substrate and fillers
ipox ER 1022	Bisphenol-A-diglycidylether monofunctional RD	189 – 213	700 – 1000	2	solvent-free epoxy systems, hydrophobic character, chemical resistant coatings
ipox ER 1042	Bisphenol-A/F-diglycidylether monofunctional RD	185 – 200	900 – 1200	1	solvent-free epoxy systems, hydrophobic character, optimized wetting of substrate and fillers
ipox ER 1042-5	Bisphenol-A/F-diglycidylether monofunctional RD	190 – 205	400 – 600	1	solvent-free epoxy systems, lower viscosity than ipox ER 1042-7
ipox ER 1042-7	Bisphenol-A/F-diglycidylether monofunctional RD	185 – 200	500 – 900	1	solvent-free epoxy systems, lower viscosity than ipox ER 1042
ipox ER 1044	Bispenol-A/F-diglycidylether, contains benzyl alcohol	200 – 225	850 – 1050	2	priming and injection resins in construction chemistry		-
ipox ER 1052	Bisphenol-A/F-diglycidylether difunctional RD	164 – 176	600 – 900	1	solvent-free epoxy systems, improved curing, very good solvent resistance
ipox ER 1052-5	Bisphenol-A/F-diglycidylether difunctional RD	164 – 176	450 – 650	1	solvent-free epoxy systems, lower viscosity than ipox ER 1052
ipox ER 1052-9	Bisphenol-A/F-diglycidylether difunctional RD	164 – 176	700 – 1000	1	solvent-free epoxy systems, higher viscosity than ipox ER 1052
ipox ER 1054	Bisphenol-A/F-diglycidylether difunctional RD	160 – 180	900 – 1400	1	solvent-free epoxy systems, very good chemical resistance
ipox ER 1062	Bisphenol-A/F-diglycidylether difunctional RD	172 – 188	700 – 1000	1	solvent-free epoxy systems, very good chemical resistance