Fast curing
even at low temperatures
ipox offers products that cure quickly even at low temperatures. And this with optimized toxicological properties. The products are, for example, free of alkylphenols or bisphenol-A and thus enable labeling without GHS 08.
show product overview
Main product category
Industry
Reactive diluents
| Product | Chemical name | Structure | CAS | EEW g/eq | Viscosity at 25ยฐC mPaโขs | Gardner colour max | Water solubility | Further attributes | Industries | Attributes | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| ipox RD 14 | Neopentylglykol-diglycidylether |  | 17557-23-2 | 150 โ 160 | 15 โ 25 | 2 | comparable to ipox RD 18; improved price/performance ratio; low volatility |      |   | ||
| ipox RD 14 eco | Neopentylglykol-diglycidylether | | 17557-23-2 | 150 โ 160 | 15 โ 25 | 2 | comparable to ipox RD 18; improved price/performance ratio; low volatility | |  | ||
| ipox RD 18 | 1,6-Hexandiol-diglycidylether |  | 933999-84-916096-31-4 | 147 โ 161 | 15 โ 25 | 1 | mechanical properties are little affected; very good chemical resistance | | | ||
| ipox RD 19 | Polyoxypropylenglycol-diglycidylether |  | 26142-30-3 Polymer | 280 โ 350 | 30 โ 70 | 1 | results in impact resistant resin systems; hydrophobic character | | | ||
| ipox RD 20 | Trimethylolpropane-polyglycidylether |  | 30499-70-8 Polymer | 140 โ 150 | 120 โ 180 | 2 | accelerating effect; high degree of crosslinking; glass transition temperature is only slightly affected | | | ||
| ipox RD 3 | 1,4-Butanediol-diglycidylether |  | 2425-79-8 | 130 โ 145 | 12 โ 22 | 1 | best difunctional thinner; mechanical properties are little affected; very good solvent resistance | | |
Bonding agents / crosslinkers
| Product | Chemical name | Structure | CAS | EEW g/eq | Viscosity at 25ยฐC mPaโขs | Gardner colour max | Water solubility | Further attributes | Industries | Attributes | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| ipox CL 12 | Glycerol-polyglycidylether |  | 90529-77-4 | 140 โ 150 | 160 โ 200 | 1 | good dilution performance; very good wetting performance; hydrophilic character | | | ||
| ipox CL 12 eco | Glycerol-polyglycidylether | | 90529-77-4 | 140 โ 150 | 160 โ 200 | 1 | good dilution performance; very good wetting performance; hydrophilic character | | | ||
| ipox CL 16 | Pentaerythritol-polyglycidylether |  | 3126-63-430973-88-7 Polymer | 156 โ 170 | 900 โ 1200 | 2 | aliphatic epoxy resin; high degree of crosslinking | | | ||
| ipox CL 16 eco | Pentaerythritol-polyglycidylether | | 3126-63-430973-88-7 Polymer | 156 โ 170 | 900 โ 1200 | 2 | aliphatic epoxy resin; high degree of crosslinking | | | ||
| ipox RD 20 | Trimethylolpropane-polyglycidylether | | 30499-70-8 Polymer | 140 โ 150 | 120 โ 180 | 2 | good dilution performance; aliphatic epoxy resin; hydrophobic character | | | ||
| ipox RD 20 eco | Trimethylolpropane-polyglycidylether | | 30499-70-8 Polymer | 140 โ 150 | 120 โ 180 | 2 | good dilution performance; aliphatic epoxy resin; hydrophobic character | | |
Modified amine hardeners
| Product | Chemical base | HEW g/eq | Viscosity at 25ยฐC mPaโขs | Gardner colour max | Gel time (min)100g,23ยฐC,DGEBA | Description | Without VOCs* | Primers | Pigmentedcoatings | Industries | Attributes | Alkylphenol free | Mortarsscreeds | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ipox EH 2078 | modified cycloaliphatic amines | 122 | 3500 โ 6500 | 3 | 30 | excellent surfaces, very good chemical resistance, curing at T > 10ยฐC | | | - | |||||
| ipox EH 2212 | MXDA-Mannichbase | 85 | 450 โ 750 | 5 | 15 | cures at T > 5ยฐC, very good chemical resistance, reactive accelerator | | | ||||||
| ipox EH 2213 | MXDA-Mannichbase | 75 | 400 โ 600 | 5 | 15 | lower viscosity than EH 2212, improved surface properties | | | ||||||
| ipox EH 2216 | modified cycloaliphatic amines | 64 | 650 โ 850 | 5 | 12 | low-temperature curing agent for epoxy resins, very fast through-curing | - | - | | | - | |||
| ipox EH 2900 | Tertiary amine | - | 90 โ 300 | 4 | - | Catalyst, Accelerator | | |